セルロ 一スナノファイバ一を添加したポリフロピレン系コンポジッ&#12488... (Japanese)

We have studied the change in the nigher order structure of polypropylene (PP)/cellulose nanofiber (CNF) composites, which have been developed in recent years, after annealing at 100°C. We found the following: CNFs suppress β crystal growth of PP in the oriented state, but do not suppress β crystal growth of PP without orientation. The amount of CNFs controls the size and orientation of PP crystals. CNFs increase the onset value of melting and crystallization. In the thermal annealing process, CNFs suppress changing of the onset value of melting, and prevent the growths of PP crystals. PP/CNF composite samples keep their shape even after thennal oxidative deterioration. As the result of the tensile testing, CNF limits elongation and increases yield stress of PP composites. [ABSTRACT FROM AUTHOR]

近年開発が進められているセルロースナノファ イバー（CNF) は， 多くの分野で注目されている材料であ り， ポリプロピレン（PP)/CNFコンポジットとして実用化 を目指して開発されつつある.しかし， 実用化で必要とさ れるPP/CNFコンポジットの結晶構造や保存性に閨する研 究はほとんど報告されていない.そこで， 筆者らは， PP/ CNFコンポジットの100°C熱促進過程におけるPPの高次構 造に関する変化， およびCNFの影響を分析し， 以下の知見 を得た.第一に， CNFは， ；8晶の形成， 結晶および配向を 抑制する.一方CNFは， 分子配向下でのPPの0 晶成長を 抑制するが， 100°C下でのPPの/3晶成長を抑制しない.ま た， CNFは， 結晶成長および結晶サイズの増大を抑制し， 融解， 結晶化におけるOn set値を上昇させる.そして， 熱 促進過程では， 融解におけるOn set値変化を抑制し， 結晶 を微細なサイズ状態に保持する.第二に， PP/CNFは， 熱 酸化劣化後も形状が安定しており， 熱促進安定性が高い.第三に， 力学強度において， CNFは伸長を制限し， 降伏応力を大 きくする.本研究は， PP成形体の高次構造変化およびPP/CNF成形体におけるCNFの機能を明確にしている. [ABSTRACT FROM AUTHOR]

Copyright of Kobunshi Ronbunshu is the property of Society of Polymer Science and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)